PA66 A3EG7巴斯夫

PA66 A3EG7巴斯夫---Ultramid A3EG7 is a 35% glass fiber reinforced injection molding PA66 grade for machinery components and housings of high stiffness and dimensional stability.

Applications

Typical applications include lamp socket housings, cooling fans, insulating profile for aluminium window frames, water containers for automotive cooling systems, as well as electrically insulating parts.

Unit system test method for physical properties after drying and adjustment
Specific gravity: 1.41 -- g / cm 3, ASTM D792, ISO 1183
Dissolution volume flow rate (MVR) (275 ° C / 5.0 kg) 40.0 -- cm 3 / 10min ISO 1133
Shrinkage flow (3.18 mm) 0.30 --%
Water absorption
Saturation 5.0 --% ASTM D570
Saturated, 23 ° C 5.0 --% ISO 62
Balanced, 50% RH 1.6 --% ASTM D570
Balanced, 23 ° C, 50% RH 1.6 --% ISO 62
Mechanical properties - unit system test method after drying and adjustment
Tensile modulus (23 ° C) 11500 8500 MPa ISO 527-2
Tensile strength
Fracture, 23 ° C 207 -- MPa ASTM D638
Fracture, 23 ° C 210 150 MPa ISO 527-2
Fracture, 80 ° C 122 -- MPa ISO 527-2
elongation
Fracture, 23 ° C 3.0 --% ASTM D638
Fracture, 23 ° C 3.0 5.0% ISO 527-2
Bending modulus
23°C 9860 -- MPa ASTM D790
23°C 10000 8480 MPa ISO 178