闽台台塑PP 1040

Market prospect of PP
PP has a broad application prospect. With the continuous progress of polymer processing equipment and the improvement of Compatibilization technology, more and more blends can be processed by dynamic vulcanization technology, which will inevitably lead to the emergence of a series of thermoplastic vulcanizates with excellent performance, convenient molding and flexible design. The traditional application fields of vulcanized rubber will be more and more replaced by thermoplastic vulcanizates The application of industrial field and life consumption field will get more rapid development. The sales volume of PP in China has been about 700000 tons a month. At present, China is one of the largest consumption countries in the world. With the colorful life, more and more PP products make consumers feel the superiority of science.
PP成型特性：
1.结晶料，吸湿性小，易发生融体破裂，长期与热金属接触易分解。
2.PP流动性好，但收缩范围及收缩值大，易发生缩孔，凹痕，变形。
3.冷却速度快，浇注系统及冷却系统应缓慢散热，并注意控制成型温度.料温低温高压时容易取向，模具温度低于55度时，塑件不光滑，易产生熔接不良，流痕，95度以上易发生翘曲变形。玻璃纤维是主要的增强材料，可以显著提高PP塑料的拉伸强度。玻纤含量一般不**过40%，一般认为在纤维长度大于0.2mm时有改性效果，其玻纤的直径在十几个微米时效果较好。玻纤含量时，增强PP的加工流动性相应下降，但仍属流动性较好的塑料

台塑集团在麦寮六轻共投资兴建十二个厂，目前各厂均已完工生产中，六轻四期扩建及去瓶颈工程大部份亦已完工。完工后除可大幅增加本公司营业额外，并纾解闽台石化基本原料不足，且可再加工生产特用化学品及工程塑料，对石化业原料取得、成本控制及产品附加提升，都有密不可分之关系，同时可促进工业升级及带动国内塑料、电子、化纤等产品之层次。

PP工艺介绍：
PP熔化温度：225-285C，注意不要**过280C。 PP模具温度：42-82C，建议使用52C。结晶程度主要由模具温度决定。
压力：可大到1850bar。
PP速度：使用高速注塑可以使内部压力减小到小。如果制品表面出现了缺陷，那么应使用较高温度下的低速注塑。
PP流道和浇口：对于冷流道,典型的流道直径范围是5-8mm。建议使用通体为圆形的注入口和流道。所有类型的浇口都可以使用。典型的浇口直径范围是1-1.5mm，但也可以使用小到0.8mm的浇口。对于边缘浇口，小的浇口深度应为壁厚的一半；小的浇口宽度应至少为壁厚的两倍。

PP属于结晶型聚合物，不到一定温度其颗粒不会熔融，不像PE 或PVC 那样在加热过程中随着温度提高而软化。一旦达到某一温度，PP颗粒迅速融化，在几度范围内就可全部转化为熔融状态。PP 的熔体粘度比较低，因此成型加工流动性良好，特别是当熔体流动速率较高时熔体粘度更小，适合于大型薄壁制品注塑成型，例如洗衣机内桶。PP属于非极性聚合物，具有良好的电绝缘性，且PP吸水性较低，电绝缘性不会受到湿度的影响。PP的介电常数、介质损耗因数都很小，不受频率及温度的影响。PP的介电强度很高，且随温度上升而。这些都是在湿、热环境下对电气绝缘材料有利的。另一方面PP的表面电阻很高，在一些场合使用必须先进行抗静电处理。