The plastics division of Taihua was originally the second division of chemical industry. In the early stage, it was established to cooperate with the development of upstream and downstream related industries in the sixth light industry plan of Formosa Plastics. At that time, it was responsible for the construction of aromatic hydrocarbon and styrene series plants. Due to the delay in the plant site of the Liuqing project, it was decided that the downstream polystyrene company should build the plant first and introduce its products into the market, so as to facilitate the production of upstream products in the future Pin.
PP力学性能 的拉伸强度和刚性都比较好，但冲击强度较差，特别是低温时耐冲击性差。此外，如果制品成型时存在取向或应力，冲击强度也会显著降低。虽然抗冲击强度差，但经过填充或增强等改性后，其机械性能在许多领域可与成本较高的工程塑料相竞争。PP 的表面硬度在五类通用塑料中属低等，仅比PE 好一些。当结晶度较高时，硬度也相应增加一些，但仍不及PVC、PS、ABS 等。热性质在五大通用塑料中，PP的耐热性是。PP 塑料制品可在100℃下长时间工作，在无外力作用时，PP制品被加热至150℃时也不会变形。

PP的化学稳定性优异，对大多数酸、碱、盐、氧化剂都显惰性。例如在100℃的浓磷酸、盐酸、40%硫酸及其它们的盐类溶液中都是稳定的，只有少数强氧化剂如发烟硫酸等才可能使其出现变化。PP是非极性化合物，对极性溶剂十分稳定，如醇、酚、醛、酮和大多数羧酸都不会使其溶胀，但在部分非极性**溶剂中容易溶解或溶胀

PP分子中存在叔碳原子，在光和热的作用下较易断裂降解。未加稳定剂的PP在150℃下被加热半小时以上，或在阳光充足的地方曝晒12天就会明显变脆。未加稳定剂的PP 粉料在室内避光放置4 个月也会严重降解，散发出明显的酸味。在PP粉料造粒之前加入0.2%以上的抗氧剂可以有效地防止PP 在加工和使用过程中的降解老化。抗氧剂分为游离基链反应终止剂（也称主抗氧剂）和过氧化物分解剂（也称辅抗氧剂）两大类，主、辅两类抗氧剂的合理配合，将会发挥良好的协同效果。PP在离开口模后，如果是在空气中缓慢冷却，就会生成较大的晶粒，制品透明度低

PP的综合性能优于PE料。PP产品质轻、韧性好、耐化学性好。PP的缺点：尺寸精度低、刚性不足、耐候性差、易产生“铜害”，它具有后收缩现象，脱模后，易老化、变脆、易变形。日常生活中，常用的保鲜盒就是由PP材料制成。为防止光老化需要在PP中加入紫外线吸收剂，它可将波290~400nm的紫外线吸收激化转化为没有破坏性的较长波长的光线。对于埋在土壤中或在室内避光使用的PP 塑料制品仅加入主辅抗氧剂即可，无须加入紫外线吸收剂。PP的收缩率和结晶度比PE低。PP对氧气、二氧化碳和水蒸汽都有一定的透过性，比起尼龙PA和聚酯PET都有明显差距，对于高阻隔性塑料，如PVDC、EVOH等就差得更多了。但与其它非塑料材料相比其气密性还是相当好的。通过添加阻隔性材料或在表面涂敷阻隔性塑料，可以提高其气密性。PP属于非极性聚合物，具有良好的电绝缘性，且PP吸水性较低，电绝缘性不会受到湿度的影响。PP的介电常数、介质损耗因数都很小，不受频率及温度的影响。PP的介电强度很高，且随温度上升而。这些都是在湿、热环境下对电气绝缘材料有利的。另一方面PP的表面电阻很高，在一些场合使用必须先进行抗静电处理