泰科纳PPS 1130L4

泰科纳PPS 1130L4---1130L4 is a 30% glass-reinforced PPS that has excellent heat and chemical resistance. It is inherently flame-retardant and exhibits high hardness and a good balance of strength and stiffness. Especially used for thin walled parts requiring long flow lengths. This grade also exhibits excellent weldability in secondary operations due to its low filler content.

Physical performance rating unit system test method

proportion

-- 1.60 g/cm³ ASTM D792

-- 1.58 g/cm³ ISO 1183

Specific volume: 0.636 cm3 / g ASTM D792

Supplementary information - rating unit system - Test methods

Specification thickness - shrink 3.18 mm internal method

Physical performance rating unit system test method

Shrinkage

Flow 0.30 to 0.50% ASTM D955

Cross flow 0.60 to 0.90% ASTM D955

Vertical flow direction 0.60 to 0.90% ISO 294-4

Flow direction 0.30 to 0.50% ISO 294-4

Water absorption (saturated, 23 ° C) 0.020% ISO 62

Hardness rating unit system test method

Rockwell hardness

Grade m 100 ASTM d785

M scale 100 ISO 2039-2

Mechanical properties rating unit system test method

Tensile modulus 12000 MPa ISO 527-2 / 1A / 1

Tensile strength

Fracture, 23 ° C 172 MPa ASTM D638

Fracture: 170 MPa ISO 527-2 / 1A / 5

elongation

Fracture, 23 ° C 1.9% ASTM D638

Fracture: 1.9% ISO 527-2 / 1A / 5

Bending modulus (23 ° C) 11000 MPa ISO 178

Bending stress 1 260 MPa ISO 178