泰科纳PPS 1140L4

泰科纳PPS 1140L4--- 1140L4 is a 40% glass-reinforced grade that is the strongest and toughest product available. It exhibits excellent heat and chemical resistance, good electrical properties and is inherently flame-retardant. The high hardness and rigidity at elevated temperatures allows for good load bearing performance. This product has good weldability due to the modest filler level. Applications made of this grade are electronical components (i.e. bobbins, lamp housings, brush holders) and various other components requiring strength and resistance to aggressive chemicals (i.e. automotive heaters, pumps, valves, fuel rails, microwave oven rings and distillation column packings).

泰科纳PPS 1140L4---物理性能 额定值 单位制 测试方法
比重 1.65 g/cm³ ASTM D792, ISO 1183
特定体积 0.611 cm³/g ASTM D792
充模分析 额定值 单位制 测试方法
Specific Heat Capacity of Melt 1500 J/kg/°C 内部方法
补充信息 额定值 单位制 测试方法
Specimen Thickness - Shrinkage 3.18 mm 内部方法
物理性能 额定值 单位制 测试方法
收缩率
    流动 0.20 到 0.30 % ASTM D955
    横向流动 0.50 到 0.70 % ASTM D955
    垂直流动方向 0.40 到 0.60 % ISO 294-4
    流动方向 0.20 到 0.60 % ISO 294-4
吸水率 (饱和, 23°C) 0.020 % ISO 62
硬度 额定值 单位制 测试方法
洛氏硬度
    M 级 100 ASTM D785
    M 计秤 100 ISO 2039-2
机械性能 额定值 单位制 测试方法
拉伸模量
    -40°C 14500 MPa ASTM D638
    75°C 11900 MPa ASTM D638
    150°C 4270 MPa ASTM D638
    200°C 3240 MPa ASTM D638
    -- 14700 MPa ISO 527-2/1A/1
抗张强度
    断裂, 23°C 200 MPa ASTM D638
    断裂 195 MPa ISO 527-2/1A/5
伸长率
    断裂, 23°C 1.7 % ASTM D638
    断裂 1.9 % ISO 527-2/1A/5
弯曲模量 (23°C) 14500 MPa ISO 178
弯曲应力 1 285 MPa ISO 178